Influence of Technological Parameters on Nanosecond Laser-induced Surface Damage of Optical Multimode Fibers

  • High-power optical multimode fibers are essential components for materials processing and surgery and can limit the reliability of expensive systems due to breakdown at the end faces. The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of the technology applied. The aim of this paper is the identification of technological parameters that are crucial for the fiber quality. Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms, which underwent different thermal treatments above the transition temperature, were tested with respect to their damage resistivity. Single and multi pulse LIDT measurements were done in accordance withHigh-power optical multimode fibers are essential components for materials processing and surgery and can limit the reliability of expensive systems due to breakdown at the end faces. The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of the technology applied. The aim of this paper is the identification of technological parameters that are crucial for the fiber quality. Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms, which underwent different thermal treatments above the transition temperature, were tested with respect to their damage resistivity. Single and multi pulse LIDT measurements were done in accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing velocities.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Markus Eberstein, Guido Mann, Jens Vogel, M. Zoheidi, Jörg KrügerORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Advanced materials research
Jahr der Erstveröffentlichung:2005
Verlag:Trans Tech Publ.
Verlagsort:Zurich
Jahrgang/Band:39-40
Erste Seite:225
Letzte Seite:230
Freie Schlagwörter:Damage threshold; Multimode fiber; Nanosecond laser; Silica glass
ISSN:1022-6680
ISSN:1662-8985
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:10.04.2008