High-temperature sliding wear, elastic modulus and transverse rupture strength of Ni bonded NbC and WC cermets
- The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS.
Autor*innen: | R. M. Genga, P. Rokebrand, L. A. Cornish, N. Nelwalani, Guido Brandt, Norbert Kelling, Mathias WoydtORCiD, A. Janse van Vuuren, C. Polese |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | International Journal of Refractory Metals & Hard Materials |
Jahr der Erstveröffentlichung: | 2020 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.5 Tribologie und Verschleißschutz | |
Verlag: | Elsevier Ltd. |
Jahrgang/Band: | 87 |
Erste Seite: | 105143 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Molybdenum carbide; Nickel; Niobium carbide; Pulse electric current sintering; Titanium carbide |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.ijrmhm.2019.105143 |
ISSN: | 0263-4368 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 28.10.2020 |
Referierte Publikation: | Nein |