Study of the surface layer of aerosil-8CB composites by TG/DTA/DSC measurements

  • Thermal analysis measurements were applied to study the behavior of composite systems containing a nematic liquid crystal (LC), 4-n-octyl-4?-cyanobiphenyl (8CB) and aerosil particles. The silica density ?s (g of silica per 1 cm3 of LC) was varied from 0.20 to 12 g/cm3 in order to approach the monomolecular structure of the surface layer. Thus, thermogravimetric (TG) measurements were performed to get information on the LC content of the samples. Moreover, they allowed an unusual application, to characterize the interaction of 8CB molecules with aerosil surface because the corresponding curves show multistep processes the temperatures of which depend on the silica density. Differential thermal analysis (DTA) also indicates several processes. Some of them, mostly due to desorption, are endothermal. Other processes are exothermal, and these are assigned to chemical transformations. The sample with silica density of 12 g/cm3 has no endothermal desorption peak at low temperatures, and hasThermal analysis measurements were applied to study the behavior of composite systems containing a nematic liquid crystal (LC), 4-n-octyl-4?-cyanobiphenyl (8CB) and aerosil particles. The silica density ?s (g of silica per 1 cm3 of LC) was varied from 0.20 to 12 g/cm3 in order to approach the monomolecular structure of the surface layer. Thus, thermogravimetric (TG) measurements were performed to get information on the LC content of the samples. Moreover, they allowed an unusual application, to characterize the interaction of 8CB molecules with aerosil surface because the corresponding curves show multistep processes the temperatures of which depend on the silica density. Differential thermal analysis (DTA) also indicates several processes. Some of them, mostly due to desorption, are endothermal. Other processes are exothermal, and these are assigned to chemical transformations. The sample with silica density of 12 g/cm3 has no endothermal desorption peak at low temperatures, and has the highest shift for the DTA peaks. It was supposed that its surface layer has a monomolecular structure. For representative samples, TG–DTA studies were supported by FTIR investigations. Thus conventional TG–DTA techniques have provided new tools to characterize the nanocomposites. Differential scanning calorimetry gives the behavior of the phase transitions. Samples with low silica density exhibit a depression of the phase transition temperatures characteristic for the bulk 8CB while those with high silica densities do not show any phase transitions.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:S. Frunza, H. Kosslick, Andreas SchönhalsORCiD, L. Frunza, I. Enache, T. Beica
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of non-crystalline solids
Jahr der Erstveröffentlichung:2003
Verlag:North-Holland Publ. Co.
Verlagsort:Amsterdam
Jahrgang/Band:325
Ausgabe/Heft:1-3
Erste Seite:103
Letzte Seite:112
DOI:10.1016/S0022-3093(03)00319-3
ISSN:0022-3093
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Bibliotheksstandort:ZJ 136
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:01.12.2003
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.