Influences of the Glass Phase on Densification, Microstructure, and Properties of Low-Temperature Co-Fired Ceramics

  • Multilayer ceramic devices based on low-temperature co-fired ceramics (LTCC) materials provide a very promising technology. Most LTCC tapes available today contain considerable fractions of glass powders to lower the sintering temperature. However, the glassy phases offer more possibilities to set a proper sintering behavior, on the one hand, and to tailor the desired properties of the final LTCC substrate, on the other. The exploitation of demixing and subsequent crystallizing glass compositions was shown on an example of a low-permittivity (4.4)—low-loss (1.5 × 103) LTCC with a high quartz content. In another LTCC material, undesired demixing could be restricted and the crystal phase anorthite could be triggered by partial dissolution of alumina in the liquid phase during sintering. To estimate the effect of silver diffusion in the latter material, the surroundings of a pure silver via were studied. A silver-contaminated range of 50 µm was detected. Using model glasses containingMultilayer ceramic devices based on low-temperature co-fired ceramics (LTCC) materials provide a very promising technology. Most LTCC tapes available today contain considerable fractions of glass powders to lower the sintering temperature. However, the glassy phases offer more possibilities to set a proper sintering behavior, on the one hand, and to tailor the desired properties of the final LTCC substrate, on the other. The exploitation of demixing and subsequent crystallizing glass compositions was shown on an example of a low-permittivity (4.4)—low-loss (1.5 × 103) LTCC with a high quartz content. In another LTCC material, undesired demixing could be restricted and the crystal phase anorthite could be triggered by partial dissolution of alumina in the liquid phase during sintering. To estimate the effect of silver diffusion in the latter material, the surroundings of a pure silver via were studied. A silver-contaminated range of 50 µm was detected. Using model glasses containing silver oxide, a strong influence of dissolved silver on viscosity and crystallization behavior of the liquid phase was demonstrated. The dielectric properties of the sintered substrates were not degraded.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Markus Eberstein, Torsten Rabe, Wolfgang Arno Schiller
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):International Journal of Applied Ceramic Technology
Jahr der Erstveröffentlichung:2006
Verlag:American Ceramic Soc.
Verlagsort:Westerville, Ohio
Jahrgang/Band:27
Ausgabe/Heft:6
Erste Seite:428
Letzte Seite:436
Freie Schlagwörter:Dielectric properties; Glass phases; LTCC; Sintering
DOI:10.1111/j.1744-7402.2006.02108.x
ISSN:1546-542X
ISSN:1744-7402
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:ZJ 138
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:07.12.2006
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.