Fretting wear of thin steel wires. Part 1: Influence of contact pressure

  • Different fretting tests of thin steel wires under different conditions (loads, strokes, number of cycles and mean pressures) were performed. The wires used had 0.45 mm in diameter and the material was a cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength over 2800 MPa. The tests were carried out with 90° "crossed cylinders" configuration varying the stroke, normal load and testing time (number of cycles). Afterwards the volumetric wear was obtained using surface profilometry with diamond stylus. With a classical study of the coefficient of wear with respect to the sliding distance, the results show that the wear coefficient increases with normal load and stroke, consequently, for the same sliding distance, the wear produced was higher when the load and/or stroke is increased. In this work, the coefficient of wear is decreasing continuously as the test is running. In order to analyze better the wear behaviour, another method, in which the volumetric wear is comparedDifferent fretting tests of thin steel wires under different conditions (loads, strokes, number of cycles and mean pressures) were performed. The wires used had 0.45 mm in diameter and the material was a cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength over 2800 MPa. The tests were carried out with 90° "crossed cylinders" configuration varying the stroke, normal load and testing time (number of cycles). Afterwards the volumetric wear was obtained using surface profilometry with diamond stylus. With a classical study of the coefficient of wear with respect to the sliding distance, the results show that the wear coefficient increases with normal load and stroke, consequently, for the same sliding distance, the wear produced was higher when the load and/or stroke is increased. In this work, the coefficient of wear is decreasing continuously as the test is running. In order to analyze better the wear behaviour, another method, in which the volumetric wear is compared with respect to the Archard's loading factor, is proposed. As result of this method, two distinctive behaviours were detected; one corresponds to the running-in period with a more aggressive wear behaviour and the second one to the stable steady state period. In all the tests the running-in period was similar with regard to the wear rates but in the stable period the wear rates were increasing with higher loads or strokes.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:A. Cruzado, Manfred Hartelt, Rolf WäscheORCiD, M.A. Urchegui, X. Gómez
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Wear
Jahr der Erstveröffentlichung:2010
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:268
Ausgabe/Heft:11-12
Erste Seite:1409
Letzte Seite:1416
Freie Schlagwörter:Contact pressure; Fretting; Unlubricated tests; Wear; Wires
DOI:10.1016/j.wear.2010.02.017
ISSN:0043-1648
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:29.04.2010
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.