Critical conditions for weld solidification crack growth
- The occurrence of solidification cracking during welding remains a little understood phenomenon, in spite of extensive studies and tests performed to evaluate and compare the relative weldability of many different alloys. From an approach often adopted in the welding community attributed to Prokhorov, solidification cracks are believed to form when a critical tensile strain is exceeded, specific to the alloy, assuming that the mushy-zone has limited ductility. Tensile stresses and strains normally form behind a moving weld pool as a result of solidification shrinkage and thermal contraction, as influenced by welding parameters and the degree of restraint.
Autor*innen: | Carl Edward Cross, Nicolas Coniglio, Philipp Schempp, M.G. Mousavi |
---|---|
Persönliche Herausgeber*innen: | J. Lippold, T. Böllinghaus, C.E. Cross, et al. |
Dokumenttyp: | Beitrag zu einem Sammelband |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Hot cracking phenomena in welds III |
Jahr der Erstveröffentlichung: | 2011 |
Verlag: | Springer |
Verlagsort: | Berlin, Heidelberg |
Ausgabe/Heft: | Part 2 |
Erste Seite: | 25 |
Letzte Seite: | 41 |
Freie Schlagwörter: | Aluminium alloy; Crack growth; Solidification cracking; Strain rate model |
DOI: | 10.1007/978-3-642-16864-2_2 |
ISBN: | 978-3-642-16863-5 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Nein |