Computational methods for lifetime prediction of metallic components under high-temperature fatigue
- The issue of service life prediction of hot metallic components subjected to cyclic loadings is addressed. Two classes of lifetime models are considered, namely, the incremental lifetime rules and the parametric models governed by the fracture mechanics concept. Examples of application to an austenitic cast iron are presented. In addition, computational techniques to accelerate the time integration of the incremental models throughout the fatigue loading history are discussed. They efficiently solve problems where a stabilized response of a component is not observed, for example due to the plastic strain which is no longer completely reversed and accumulates throughout the fatigue history. The performance of such an accelerated Integration technique is demonstrated for a finite element simulation of a viscoplastic solid under repeating loading–unloading cycles.
Autor*innen: | Vitaliy Kindrachuk, Bernard FedelichORCiD, Birgit RehmerORCiD, Frauke Peter |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Metals |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
5 Werkstofftechnik / 5.5 Materialmodellierung | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | mdpi |
Verlagsort: | Basel, Switzerland |
Jahrgang/Band: | 9 |
Ausgabe/Heft: | 4 |
Erste Seite: | 390, 1 |
Letzte Seite: | 24 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Fatigue; Finite element analysis; Incremental lifetime models |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.3390/met9040390 |
URN: | urn:nbn:de:kobv:b43-481215 |
URL: | https://www.mdpi.com/2075-4701/9/4/390 |
ISSN: | 2075-4701 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 03.06.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 03.06.2019 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |