Solidification cracking in laser GMA hybrid welding of thick-walled parts

  • Laser GMA hybrid welds, producing partial penetration, were conducted on stiff tubes made of S460NH. Experiments, using a design-of-experiments plan were conducted to examine the influence of the welding parameters on the occurrence of solidification cracks. Results say that cracks diminish, when high levels of arc power are applied, while their number increases with rising laser beam power. The weld velocity had no measurable impact.

Volltext Dateien herunterladen

  • Solidification cracking in laser GMA hybrid welding of thick walled parts.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:M.O. Gebhardt, Andrey GumenyukORCiD, Michael RethmeierORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Science and technology of welding and joining
Jahr der Erstveröffentlichung:2014
Herausgeber (Institution):Institute of Materials, Minerals and Mining
Verlag:Maney
Verlagsort:London
Jahrgang/Band:19
Ausgabe/Heft:3
Erste Seite:209
Letzte Seite:213
Freie Schlagwörter:Design of experiments; Laser hybrid welding; Partial penetration welding; Solidification cracking; Thick walled parts; Tube welding
DOI:10.1179/1362171813Y.0000000171
ISSN:1362-1718
ISSN:1743-2936
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:06.03.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.