Maghemite Nanoparticles Protectively Coated with Poly(ethylene imine) and Poly(ethylene oxide)-block-poly(glutamic acid)

  • Superparamagnetic iron oxide particles (SPIO) of maghemite were prepared in aqueous solution and subsequently stabilized with polymers in two layer-by-layer deposition steps. The first layer around the maghemite core is formed by poly(ethylene imine) (PEI), and the second one is formed by poly(ethylene oxide)-block-poly(glutamic acid) (PEO-PGA). The hydrodynamic diameter of the particles increases stepwise from Dh = 25 nm (parent) via 35 nm (PEI) to 46 nm (PEI plus PEO-PGA) due to stabilization. This is accompanied by a switching of their -potentials from moderately positive (+28 mV) to highly positive (+50 mV) and finally slightly negative (-3 mV). By contrast, the polydispersity indexes of the particles remain constant (ca. 0.15). Mössbauer spectroscopy revealed that the iron oxide, which forms the core of the particles, is only present as Fe(III) in the form of superparamagnetic maghemite nanocrystals. The magnetic domains and the maghemite crystallites were found to be identicalSuperparamagnetic iron oxide particles (SPIO) of maghemite were prepared in aqueous solution and subsequently stabilized with polymers in two layer-by-layer deposition steps. The first layer around the maghemite core is formed by poly(ethylene imine) (PEI), and the second one is formed by poly(ethylene oxide)-block-poly(glutamic acid) (PEO-PGA). The hydrodynamic diameter of the particles increases stepwise from Dh = 25 nm (parent) via 35 nm (PEI) to 46 nm (PEI plus PEO-PGA) due to stabilization. This is accompanied by a switching of their -potentials from moderately positive (+28 mV) to highly positive (+50 mV) and finally slightly negative (-3 mV). By contrast, the polydispersity indexes of the particles remain constant (ca. 0.15). Mössbauer spectroscopy revealed that the iron oxide, which forms the core of the particles, is only present as Fe(III) in the form of superparamagnetic maghemite nanocrystals. The magnetic domains and the maghemite crystallites were found to be identical with a size of 12.0 ± 0.5 nm. The coated maghemite nanoparticles were tested to be stable in water and in physiological salt solution for longer than 6 months. In contrast to novel methods for magnetic nanoparticle production, where organic solvents are necessary, the procedure proposed here can dispense with organic solvents. Magnetic resonance imaging (MRI) experiments on living rats indicate that the nanoparticles are useful as an MRI contrast agent.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Andreas ThünemannORCiD, D. Schütt, L. Kaufner, U. Pison, H. Möhwald
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Langmuir
Jahr der Erstveröffentlichung:2006
Verlag:American Chemical Society
Verlagsort:Washington, DC
Jahrgang/Band:22
Ausgabe/Heft:5
Erste Seite:2351
Letzte Seite:2357
Freie Schlagwörter:Mössbauer; Polyelectrolyte; Polymer
DOI:10.1021/la052990d
ISSN:0743-7463
ISSN:1520-5827
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:02.03.2006
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.