Reaction of CO2 gas with (radicals in) plasma-polymerized acrylic acid (and formation of COOH-rich polymer layers)

  • In contrast to most of the existing literature on plasma polymerization of acrylic acid (AA), not only the chemical structure and film thickness of the deposits were studied, but also a new way to obtain COOH-rich surfaces. This is an important aspect when applying the obtained coatings for biomedical and electronics applications. Therefore, acrylic acid/CO2 polymer films with a thickness of ca. 150 nm were deposited in the pulsed plasma regime onto polyethylene and aluminium as organic and inorganic substrates. Their structure–property relationships were studied in dependence on the mixture ratio of acrylic acid monomer and CO2 gas. The influence of the CO2 gas on the regularity and functionality of plasma deposited poly(acrylic acid) (PAA) was studied in detail using bulk-sensitive (dielectric spectroscopy and Fourier transforms infrared spectroscopy) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy. For a clear identification of the functionality of theIn contrast to most of the existing literature on plasma polymerization of acrylic acid (AA), not only the chemical structure and film thickness of the deposits were studied, but also a new way to obtain COOH-rich surfaces. This is an important aspect when applying the obtained coatings for biomedical and electronics applications. Therefore, acrylic acid/CO2 polymer films with a thickness of ca. 150 nm were deposited in the pulsed plasma regime onto polyethylene and aluminium as organic and inorganic substrates. Their structure–property relationships were studied in dependence on the mixture ratio of acrylic acid monomer and CO2 gas. The influence of the CO2 gas on the regularity and functionality of plasma deposited poly(acrylic acid) (PAA) was studied in detail using bulk-sensitive (dielectric spectroscopy and Fourier transforms infrared spectroscopy) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy. For a clear identification of the functionality of the deposited films, the COOH groups were estimated after derivatization with trifluoroethanol by XPS measurement as well as by the quantitative analysis of the FTIR data. Results show, in presence of a small amount of CO2 gas within the acrylic acid plasma, a structure of poly(acrylic acid) with high concentration of COOH groups was obtained. However, the excess of CO2 gas in the plasma chamber leads to fragmentation of the monomer or/and degradation of the layer which is already deposited. A polymer network is obtained with an increasing abundance of branched groups for AA/CO2 with increasing CO2 gas in the mixture.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Fahmy, Schönhals - Reaction of CO2 gas with (radicals in) plasma-polymerized acrylic acid (and formation of COOH-rich polymer layers).pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Alaa Fahmy, Andreas SchönhalsORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Plasma Processes and Polymers
Jahr der Erstveröffentlichung:2016
Verlag:Wiley-VCH Verlag
Verlagsort:Weinheim
Jahrgang/Band:13
Ausgabe/Heft:5
Erste Seite:499
Letzte Seite:508
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:COOH rich surfaces; Plasma polymerization; Poly(acrylic acid)
DOI:10.1002/ppap.201500128
ISSN:1612-8850
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:17.05.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:25.07.2016
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.