Temperature response of self-assembled micelles of telechelic hydrophobically modified Poly(2-alkyl-2-oxazoline)s in water

  • Hydrophobically end-modified (HM) poly(2-ethyl-2-oxazolines) (PEtOx) and poly(2-isopropyl-2-oxazolines) (PiPrOx) bearing an n-octadecyl chain on both termini or on one chain end only were prepared by cationic ring-opening polymerization of 2-ethyl-2-oxazoline and 2-isopropyl-2-oxazoline, respectively, and subsequent end-group modification. The polymers had a molar mass (Mn) ranging from 7000 to 13000 g mol-1, a size distribution Mw/Mn < 1.20, and end-group functionality > 0.97. All polymers, except the semitelechelic sample C18-PiPrOx-OH 13K (Mn = 13000 g mol-1), formed core-shell micelles in cold water with a hydrodynamic radius (RH), measured by dynamic light scattering, between 7 and 12 nm and a core of radius (Rc), determined by analysis of small-angle X-ray scattering (SAXS) data, of ~1.3 nm. Aqueous solutions of all polymers underwent a heat-induced phase transition detected by an increase in solution turbidity at a temperature (Tcp, cloud point) ranging from 32 to 62 °C,Hydrophobically end-modified (HM) poly(2-ethyl-2-oxazolines) (PEtOx) and poly(2-isopropyl-2-oxazolines) (PiPrOx) bearing an n-octadecyl chain on both termini or on one chain end only were prepared by cationic ring-opening polymerization of 2-ethyl-2-oxazoline and 2-isopropyl-2-oxazoline, respectively, and subsequent end-group modification. The polymers had a molar mass (Mn) ranging from 7000 to 13000 g mol-1, a size distribution Mw/Mn < 1.20, and end-group functionality > 0.97. All polymers, except the semitelechelic sample C18-PiPrOx-OH 13K (Mn = 13000 g mol-1), formed core-shell micelles in cold water with a hydrodynamic radius (RH), measured by dynamic light scattering, between 7 and 12 nm and a core of radius (Rc), determined by analysis of small-angle X-ray scattering (SAXS) data, of ~1.3 nm. Aqueous solutions of all polymers underwent a heat-induced phase transition detected by an increase in solution turbidity at a temperature (Tcp, cloud point) ranging from 32 to 62 °C, depending on polymer structure and size. Temperature-dependent light scattering (LS) measurements and fluorescence depolarization studies with the probe diphenylhexatriene (DPH) revealed that extensive intermicellar bridging takes place in solutions heated in the vicinity of Tcp leading to large assemblies (RH ≥ 1 µm). Further heating caused these assemblies to shrink into objects with RH ~ 300-700 nm, depending on the size and structure of the polymer. The formation of H-bonds between water molecules and the main-chain amide nitrogen atoms imparts distinct features to the flower/star micelles formed by telechelic/semitelechelic PiPrOx and PEtOx, compared to the micelles formed by other hydrophobically end-modified water-soluble polymers, such as poly(ethylene oxide) or poly(N-isopropylacrylamide).zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:R. Obeid, Elena Maltseva, Andreas ThünemannORCiD, F. Tanaka, F. M. Winnik
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Macromolecules
Jahr der Erstveröffentlichung:2009
Verlag:American Chemical Society
Verlagsort:Washington, DC
Jahrgang/Band:42
Ausgabe/Heft:6
Erste Seite:2204
Letzte Seite:2214
DOI:10.1021/ma802592f
ISSN:0024-9297
ISSN:1520-5835
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:23.03.2009
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.