Electromagnetic control of the weld pool dynamics in partial penetration laser beam welding of aluminium alloys

  • An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction. The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM) induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM) contribution to the surface tension (the Garnier-Moreau effect)

Volltext Dateien herunterladen

  • Electromagnetic control of the weld pool dynamics in partial penetration laser beam welding of aluminium alloys.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Vjaceslav Avilov, André Schneider, Marco Lammers, Andrey Gumenyuk, Michael Rethmeier
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):ICALEO 2012 - 31st International congress on applications of lasers & electro-optics (Proceedings)
Jahr der Erstveröffentlichung:2012
Herausgeber (Institution):Laser Institute of America (LIA)
Ausgabe/Heft:Paper 701
Erste Seite:250
Letzte Seite:256
Veranstaltung:ICALEO 2012 - 31st International congress on applications of lasers & electro-optics
Veranstaltungsort:Anaheim, CA, USA
Beginndatum der Veranstaltung:23.09.2012
Enddatum der Veranstaltung:27.09.2012
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein