Rapid fabrication of porous Si3N4/SiC ceramics via nitridation of silicon powder with ZrO2 as catalyst

  • Porous Si3N4/SiC ceramics were rapidly prepared with Y2O3 as sintering additive and ZrO2 as nitrided catalyst, using Si and SiC as starting powders. Porous Si3N4/SiC ceramics with 5 wt% ZrO2 addition showed a complete nitridation and good mechanical properties (with a high porosity of 34.96%, flexural strength of 150±4.2 MPa, linear shrinkage of 0.02%). It was revealed that the reciprocal formation of ZrO2 and ZrN effectively enhanced nitridation by inhibiting the melting of silicon in micro-regions.

Volltext Dateien herunterladen

  • 1-s2.0-S0272884213015538-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:H.-L. Hu, Y.-P. Zeng, Y. Xia, Dongxu Yao, K.-H. Zuo, Jens GünsterORCiD, J.G. Heinrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Ceramics international
Jahr der Erstveröffentlichung:2014
Verlag:Ceramurgia
Verlagsort:Faenza
Jahrgang/Band:40
Ausgabe/Heft:5
Erste Seite:7579
Letzte Seite:7582
Freie Schlagwörter:D. ZrO2; Rapid nitridation; Si3N4/SiC porous ceramics
DOI:10.1016/j.ceramint.2013.11.098
ISSN:0272-8842
ISSN:1873-3956
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:06.03.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.