Porous Si3N4 ceramics prepared via partial nitridation and SHS

  • Porous Si3N4 ceramics were prepared via partial nitridation and self-propagating high temperature synthesis (SHS) process. Raw Si and additive Y2O3 were mixed and molded under 10 MPa into a compact, the compact was partial nitridation at 1300 °C to form a porous Si/Si3N4, and then it was buried in a Si/Si3N4 bed for SHS to obtain porous Si3N4 with rod-like β-Si3N4 morphology. The processing combined the advantages of the nitridation of Si and SHS with low cost, low shrinkage and time saving. Porous Si3N4 with a porosity of 47%, a strength of 143 MPa were obtained by this method.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Dongxu Yao, Y. Xia, K.-h. Zuo, D. Jiang, Jens Günster, Y.-P. Zeng, J.G. Heinrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of the European Ceramic Society
Jahr der Erstveröffentlichung:2013
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.4 Keramische Prozesstechnik und Biowerkstoffe
Herausgeber (Institution):European Ceramic Society
Verlag:Elsevier
Verlagsort:Oxford
Jahrgang/Band:33
Ausgabe/Heft:2
Erste Seite:371
Letzte Seite:374
Freie Schlagwörter:Porosity; Si3N4; Strength
DOI:https://doi.org/10.1016/j.jeurceramsoc.2012.08.033
ISSN:0955-2219
ISSN:1873-619X
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:01.09.2014