Zirconium-based coatings in highly stressed rolling contacts as alternative solution to DLC and ta-C coatings

  • The slip-rolling resistance of DLC, a-C and ta-C thin film coatings was improved considerably in the last years, but there is still room for improvements in relation to (a) the temperature stability and (b) initial surface roughness after deposition. This paper presents a novel coating-substrate system in comparison to recently developed DLC coatings in a bench-mark test procedure exerting slip-rolling conditions in the presence of liquid lubricants. One of the Zr-based thin film coatings can withstand at least 1 million cycles under initial Hertzian contact pressures of up to P0max = 3500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions or ten million of cycles under P0max = 2940 MPa. In comparison, some of the newly developed DLC coatings are slip-rolling resistant for at least up to 10 million cycles at RT (some of them also at 120 °C oil temperature) under Hertzian contact pressures of Pmax = 2600/2940 MPa. InThe slip-rolling resistance of DLC, a-C and ta-C thin film coatings was improved considerably in the last years, but there is still room for improvements in relation to (a) the temperature stability and (b) initial surface roughness after deposition. This paper presents a novel coating-substrate system in comparison to recently developed DLC coatings in a bench-mark test procedure exerting slip-rolling conditions in the presence of liquid lubricants. One of the Zr-based thin film coatings can withstand at least 1 million cycles under initial Hertzian contact pressures of up to P0max = 3500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions or ten million of cycles under P0max = 2940 MPa. In comparison, some of the newly developed DLC coatings are slip-rolling resistant for at least up to 10 million cycles at RT (some of them also at 120 °C oil temperature) under Hertzian contact pressures of Pmax = 2600/2940 MPa. In general, Zr-based thin film coatings do not require special formulated oil formulations and Zr(C,N) bear on a straight coating architecture suited for mass production with nanosized layers.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Charles-Alix Manier, H. Ziegele, J. Barriga, J. Goikoetxea, Mathias WoydtORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Wear
Jahr der Erstveröffentlichung:2010
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:269
Ausgabe/Heft:11-12
Erste Seite:770
Letzte Seite:781
Freie Schlagwörter:DLC; Multilayer; Nanostructured coating; Slip-rolling resistance; Zirconium; Zr(C,N)
DOI:10.1016/j.wear.2010.08.004
ISSN:0043-1648
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:11.11.2010
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.