Evaluation of heat treatment performance of potential pipe steels in CCS-environment

  • To resist the corrosive geothermal environment during carbon capture and storage CCS -such as: heat, pressure, salinity of the aquifer, CO2-partial pressure, properties of pipe steels-require certain specification. For evaluation samples of differently heat treated high alloyed stainless injection-pipe steels AISI 420 X46Cr13, AISI 420J X20Cr13 as well as X5CrNiCuNb16–4 AISI 630 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h up to 8000 h in a CO2-saturated synthetic aquifer environment similar to a possible geological situation in the northern German Basin. Corrosion rates and scale growth are lowest after long term exposure for steels hardened and tempered at 600 °C to 670 °C and pits -indicating local corrosion- decrease in diameter but increase in number as a function of carbon content of the steel. Martensitic microstructure is preferred with respect to these particular conditions.

Volltext Dateien herunterladen

  • Evaluation of heat treatment performance of potential pipe steels in CCS-environment.pdf

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Autoren/innen:A. Pfennig, Helmut Wolthusen, Philip Zastrow, Axel Kranzmann
Persönliche Herausgeber/innen:A. Jha, C. Wang, N.R. Neelameggham, D.P. Guillen, L. Li, C.K. Belt, R. Kirchain, J.S. Spangenberger, F. Johnson, A.J. Gomes, A. Pandey, P. Hosemann
Dokumenttyp:Beitrag zu einem Sammelband
Titel des übergeordneten Werkes (Englisch):Energy Technology 2015: Carbon Dioxide Management and Other Technologies
Jahr der Erstveröffentlichung:2015
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.1 Materialographie, Fraktographie und Alterung technischer Werkstoffe
Herausgeber (Institution):The Minerals, Metals & Materials Society (TMS)
Erste Seite:15
Letzte Seite:22
Freie Schlagwörter:Aquifer; CCS; Carbon storage; Corrosion; High pressure; High temperature
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein