Suitable test method for the determination of the environmental stress cracking behaviour of polyethylene terephthalate as material for dangerous goods packagings

  • The chemical industry has expressed great interest in using polyethylene terephthalate (PET) as material for packagings for the transport of dangerous goods. Due to the high strength and stiffness of PET, the wall thickness and weight of packagings can be reduced. The aim of this work was to find a laboratory test method for the determination of the stress cracking resistance of PET. One test method is the Full Notch Creep Test (FNCT), which was developed for polyethylene (PE) and is described in the standards EN ISO 13274 and EN 15507. It was investigated whether testing specimens made of PET with a full coplanar notch around the middle of the specimens show weakening after the impact of a tensile force in a wetting solution at 50°C. Unfortunately, this method couldn’t be used for PET because the specimens broke during notching due to the high brittleness of PET. The molding of the sheets and the following temper process for twelve hours are very time-consuming, Another possibilityThe chemical industry has expressed great interest in using polyethylene terephthalate (PET) as material for packagings for the transport of dangerous goods. Due to the high strength and stiffness of PET, the wall thickness and weight of packagings can be reduced. The aim of this work was to find a laboratory test method for the determination of the stress cracking resistance of PET. One test method is the Full Notch Creep Test (FNCT), which was developed for polyethylene (PE) and is described in the standards EN ISO 13274 and EN 15507. It was investigated whether testing specimens made of PET with a full coplanar notch around the middle of the specimens show weakening after the impact of a tensile force in a wetting solution at 50°C. Unfortunately, this method couldn’t be used for PET because the specimens broke during notching due to the high brittleness of PET. The molding of the sheets and the following temper process for twelve hours are very time-consuming, Another possibility is laid down in BAM’s Dangerous Goods Rule BAM-GGR 015. This test was carried out with 1l PET bottles, which were filled with a 5% wetting solution and mounted with a clamping tool for 28 days at 40°C. Tensile test specimens were cut out afterwards from the middle of the bottles in the deformed areas. The tensile properties of the PET specimens couldn’t be determined due to the hardness of the material. In conclusion, the only way to provide information about the stress cracking resistance of PET was to perform stacking tests with PET design types of packagings. 1l bottles made of PET were filled with a 5% wetting solution and stored with a stacking load for 28 days at 40°C according to EN ISO 16495. The test bottles of PET passed the stacking tests.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 201700690_Weltschev_Frontiers in Polymer Science.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Margit Weltschev
Koautor*innen:Stefanie Schwarzer, Mario Eiben
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Dangerous goods packaging; Laboratory method; Polyethylene terephthalate; Stress cracking resistance
Veranstaltung:Fifth International Symposium Frontiers in Polymer Science
Veranstaltungsort:Seville, Spain
Beginndatum der Veranstaltung:17.05.2017
Enddatum der Veranstaltung:19.05.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:01.06.2017
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.