NbC grain growth control and mechanical properties of Ni bonded NbC cermets prepared by vacuum liquid phase sintering

  • The current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) additions on the microstructure and concommitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. All cermets were prepared by pressureless sintering in vacuum. Detailed microstructural investigation was performed by electron probe microanalysis (EPMA) and X-ray diffraction (XRD) analysis. Sintering results indicated that both the sintering temperature and secondary carbide additions had a significant effect on the properties of NbC-Ni cermets. Nickel pools and residual pores were observed in the cermets sintered at temperatures ≤ 1340 °C. Increasing of the sintering temperature up to 1420 or 1480 °C resulted in fully densified NbC-Ni based cermets composed of homogeneous contrast cubic NbC grains for the single carbide (VC or Mo2C) modyfied system, whereas core-rim structured NbC grains were observed with the additon of TiC + VC or TiC+Mo2C. TheThe current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) additions on the microstructure and concommitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. All cermets were prepared by pressureless sintering in vacuum. Detailed microstructural investigation was performed by electron probe microanalysis (EPMA) and X-ray diffraction (XRD) analysis. Sintering results indicated that both the sintering temperature and secondary carbide additions had a significant effect on the properties of NbC-Ni cermets. Nickel pools and residual pores were observed in the cermets sintered at temperatures ≤ 1340 °C. Increasing of the sintering temperature up to 1420 or 1480 °C resulted in fully densified NbC-Ni based cermets composed of homogeneous contrast cubic NbC grains for the single carbide (VC or Mo2C) modyfied system, whereas core-rim structured NbC grains were observed with the additon of TiC + VC or TiC+Mo2C. The secondary carbide doped cermets with 5–10 vol.% VC/Mo2C and 10 vol.% TiC showed a significantly improved hardness and fracture toughness, as compared to the plain NbC-Ni cermets.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Woydt_Plansee_2017_HM 13.pdf
    eng
  • 19th Plansee Seminar 2017.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:S. G. Huang, J. Vleugels, H. Mohrbacher, Mathias WoydtORCiD
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):International Conference on Refractory Metals and Hard Materials- 19th Plansee seminar
Jahr der Erstveröffentlichung:2017
Erste Seite:HM 13/1
Letzte Seite:HM 13/11
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Cermet; Core-rim; Hard materials; Mechanical properties; Microstructure; Sintering
Veranstaltung:19. Plansee Seminar
Veranstaltungsort:Reutte, Austria
Beginndatum der Veranstaltung:29.05.2017
Enddatum der Veranstaltung:02.06.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:14.06.2017
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.