Accelerated aging of polyethylene materials at high oxygen pressure characterized by photoluminescence spectroscopy and established aging characterization methods

  • Two commercial polyethylene grades were exposed to water at elevated temperatures and enhanced oxygen pressure. To characterize their aging behavior laser-induced photoluminescence spectroscopy was applied. Additionally, aging characterization was performed by established methods such as tensile testing, infrared (IR) spectroscopy, high performance liquid chromatography (HPLC), differential scanning calorimetry (DSC) and UV–VIS spectroscopy. During the initial stages of aging, the overall concentration of phenolic antioxidants as well as oxidation onset temperatures decreased exponentially. Simultaneously, significant discoloration due to the formation of conjugated degradation products from phenolic antioxidants (e.g., quinone methides) was detected. After the consumption of antioxidants, photoluminescence started to grow continuously presumably due to the formation of photoluminescent unsaturated carbonyls. In the final stages of aging, embrittlement of the materials as characterizedTwo commercial polyethylene grades were exposed to water at elevated temperatures and enhanced oxygen pressure. To characterize their aging behavior laser-induced photoluminescence spectroscopy was applied. Additionally, aging characterization was performed by established methods such as tensile testing, infrared (IR) spectroscopy, high performance liquid chromatography (HPLC), differential scanning calorimetry (DSC) and UV–VIS spectroscopy. During the initial stages of aging, the overall concentration of phenolic antioxidants as well as oxidation onset temperatures decreased exponentially. Simultaneously, significant discoloration due to the formation of conjugated degradation products from phenolic antioxidants (e.g., quinone methides) was detected. After the consumption of antioxidants, photoluminescence started to grow continuously presumably due to the formation of photoluminescent unsaturated carbonyls. In the final stages of aging, embrittlement of the materials as characterized by the degradation of mechanical properties (i.e., loss in ductility) coincided with rising carbonyl index values as well as an increase in crystallinity due to chemicrystallization. Between integrated photoluminescence intensity and carbonyl index, a linear correlation was established. In the induction period, the photoluminescence method exhibited a significantly higher sensitivity to reflect aging induced material changes.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S0141391014002584-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:K. Grabmayer, G.M. Wallner, S. Beißmann, Ulrike BraunORCiD, R. Steffen, D. Nitsche, B. Röder, W. Buchberger, R.W. Lang
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer degradation and stability
Jahr der Erstveröffentlichung:2014
Verlag:Applied Science Publ.
Verlagsort:London
Jahrgang/Band:109
Erste Seite:40
Letzte Seite:49
Freie Schlagwörter:Aging; High oxygen pressure; PE-RT; Photoluminescence spectroscopy; Polyethylene
DOI:10.1016/j.polymdegradstab.2014.06.021
ISSN:0141-3910
ISSN:1873-2321
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:11.09.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.