Time- and space-resolved dynamics of ablation and optical breakdown induced by femtosecond laser pulses in indium phosphide

  • Femtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by single intense 130 fs laser pulses in single-crystalline (100)-indium phosphide wafers in air on a time scale from ~100 fs up to 8 ns. In the ablative regime close to the ablation threshold, transient surface reflectivity patterns are observed by fs microscopy on a ps to ns time scale as a consequence of the complex spatial density structure of the ablating material (dynamic Newton fringes). At higher fluences, exceeding six times the ablation threshold, optical breakdown causes another, more violent ablation regime, which reduces the energy deposition depth along with the time of significant material removal. As a consequence, ablation lasts longer in a ring-shaped region around the region of optical breakdown. This leads to the formation of a crater profile with a central protrusion. In the melting regime below the ablationFemtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by single intense 130 fs laser pulses in single-crystalline (100)-indium phosphide wafers in air on a time scale from ~100 fs up to 8 ns. In the ablative regime close to the ablation threshold, transient surface reflectivity patterns are observed by fs microscopy on a ps to ns time scale as a consequence of the complex spatial density structure of the ablating material (dynamic Newton fringes). At higher fluences, exceeding six times the ablation threshold, optical breakdown causes another, more violent ablation regime, which reduces the energy deposition depth along with the time of significant material removal. As a consequence, ablation lasts longer in a ring-shaped region around the region of optical breakdown. This leads to the formation of a crater profile with a central protrusion. In the melting regime below the ablation threshold, the melting dynamics of indium phosphide has been quantified and subsequent superficial amorphization has been observed upon solidification on the ns time scale leading to amorphous layer thicknesses of the order of a few tens of nanometers.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 2008_Bonse_Journal_of_Applied_Physics_103_054910.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Jörn BonseORCiD, G. Bachelier, J. Siegel, J. Solis, Heinz SturmORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of applied physics
Jahr der Erstveröffentlichung:2008
Verlag:American Institute of Physics
Verlagsort:Melville, NY
Jahrgang/Band:103
Ausgabe/Heft:5
Erste Seite:054910-1
Letzte Seite:054910-6
Freie Schlagwörter:Ablation; Femtosecond laser pulse; Fs-time resolved microscopy; Indium Phosphide; Scanning Force Microscopy; Surface reflectivity
DOI:10.1063/1.2885105
ISSN:0021-8979
ISSN:1089-7550
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:31.03.2008
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.