X-ray refraction radiography. Case study: the thermal microcracking in ZrO2-SiO2 after application of external loads at high temperatures
- This study is shown as an example of the potential of synchrotron X-ray refraction technique to determine the evolution of damage in brittle (microcracked) materials. The strength of X-ray refraction resides in its high detectability of features (e.g., cracks, pores) within large volumes, enabling a macroscopic characterization of the microstructure. The case study is a Zirconia-based cast refractory, which is aimed to function at high temperatures (even in excess of 1700°C) in industrial furnaces to enable the production of special glasses. Therefore, this material must withstand severe in-service conditions (both thermomechanical and chemical). X-ray refraction technique is used to monitor the microcracking evolution of the material, which was previously subjected to thermal cycles (crossing the martensitic phase transformation around 1000°C) at two different stress levels.
Autor*innen: | Itziar Serrano MunozORCiD |
---|---|
Weitere Person: | René LaquaiORCiD, Bernd R. MüllerORCiD, M. Huger, T. Chotard, G. Antou, Giovanni BrunoORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 8 Zerstörungsfreie Prüfung |
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Monoclinic to tetragonal transformation; Refractory zirconia; Synchrotron refraction radiography; Thermally induced microcracking |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | Euromat 2021 |
Veranstaltungsort: | Online meeting |
Beginndatum der Veranstaltung: | 13.09.2021 |
Enddatum der Veranstaltung: | 17.09.2021 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 15.09.2021 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |