Wear behaviour of MgO stabilized zirconia in hot steam environment up to 400°C
- Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
Autor*innen: | Rolf WäscheORCiD, K. Sato, Guido Brandt, Thomas SchmidORCiD, S. Sasaki, Mathias WoydtORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Wear |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 1 Analytische Chemie; Referenzmaterialien |
1 Analytische Chemie; Referenzmaterialien / 1.4 Prozessanalytik | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.5 Tribologie und Verschleißschutz | |
Verlag: | Elsevier B.V. |
Jahrgang/Band: | 426-427 |
Erste Seite: | 428 |
Letzte Seite: | 432 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Friction; Hot steam; Raman spectroscopy; Tribofilm; Wear; Zirconia |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.wear.2019.01.047 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 29.04.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 06.05.2019 |