Short and long term degradation behaviour of Mg-1Ca magnesium alloys and protective coatings based on plasma-chemical oxidation and biodegradable polymer coating in synthetic body fluid

  • The main problem limiting the application of magnesium alloys as biodegradable implant material is its high degradation rate. In order to slow down the corrosion rate an extrusion process and specific coating systems based on plasma-chemical oxidation (PCO) and organic dip coating with poly(ʟ-lactid-co-caprolacton) (PLLC) were applied on Mg–1Ca magnesium alloy. The additional PLLC coating is used to delay the start of substrate corrosion, while the purpose of the PCO coating is to decrease the substrate corrosion rate. The corrosion behaviour was investigated in synthetic body fluid (SBF) through measurement of the hydrogen evolution rate in long term tests and polarisation and electrochemical noise measurements in short term tests. The results showed significant differences between the cast and extruded alloys and a decrease of the corrosion rate due to corrosion product formation. The combination of both coating systems resulted in a significant delay of metal substrate corrosion andThe main problem limiting the application of magnesium alloys as biodegradable implant material is its high degradation rate. In order to slow down the corrosion rate an extrusion process and specific coating systems based on plasma-chemical oxidation (PCO) and organic dip coating with poly(ʟ-lactid-co-caprolacton) (PLLC) were applied on Mg–1Ca magnesium alloy. The additional PLLC coating is used to delay the start of substrate corrosion, while the purpose of the PCO coating is to decrease the substrate corrosion rate. The corrosion behaviour was investigated in synthetic body fluid (SBF) through measurement of the hydrogen evolution rate in long term tests and polarisation and electrochemical noise measurements in short term tests. The results showed significant differences between the cast and extruded alloys and a decrease of the corrosion rate due to corrosion product formation. The combination of both coating systems resulted in a significant delay of metal substrate corrosion and all coating systems showed good correlation between short and long term tests. The combination of the three investigation methods provides the possibility to gain more information about the degradation behaviour and break down of protective coatings.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:P. Rosemann, J. Schmidt, Andreas Heyn
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials and corrosion
Jahr der Erstveröffentlichung:2013
Herausgeber (Institution):Gesellschaft für Korrosionsschutz
Verlag:Wiley-VCH Verl.
Verlagsort:Weinheim
Jahrgang/Band:64
Ausgabe/Heft:8
Erste Seite:714
Letzte Seite:722
Freie Schlagwörter:Coatings; Corrosion; Electrochemical noise; Magnesium; Plasma-chemical oxidation
DOI:10.1002/maco.201206590
ISSN:0947-5117
ISSN:1521-4176
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:16.09.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.