Electromagnetic porosity Reduction in Laser Beam Welding of Die-Cast Aluminum Alloy
- The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied.
Autor*innen: | André Fritzsche, Kai HilgenbergORCiD, F. Teichmann, H. Pries, Michael RethmeierORCiD |
---|---|
Dokumenttyp: | Beitrag zu einem Tagungsband |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Lasers in Manufacturing Conference 2017 |
Jahr der Erstveröffentlichung: | 2017 |
Erste Seite: | 1 |
Letzte Seite: | 10 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Die-cast aluminum; Electromagnetic influence; Laser beam welding; Porosity reduction |
Veranstaltung: | Lasers in Manufacturing Conference 2017 |
Veranstaltungsort: | Munich, Germany |
Beginndatum der Veranstaltung: | 26.06.2017 |
Enddatum der Veranstaltung: | 29.06.2017 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 08.08.2017 |
Referierte Publikation: | Nein |