Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets
- Test procedure to characterize the cracking susceptibility of RSW-steels has been developed During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel Complex phase steels behavior during test procedure: Crack length growth with increasing force could not be determined The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case) 30
Autor*innen: | Michael RethmeierORCiD |
---|---|
Koautor*innen: | H. Suwala, Andrey GumenyukORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2015 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Externally loaded hot cracking test; Self-restraint hot cracking; Variables influencing hot cracking; Welding jig |
Veranstaltung: | The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference |
Veranstaltungsort: | Düsseldorf, Germany |
Beginndatum der Veranstaltung: | 15.06.2015 |
Enddatum der Veranstaltung: | 19.06.2015 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 21.11.2016 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |