Microstructure characterization of the Inconel 686 clad layer after high-temperature corrosion tests in aggressive gases and ashes
- The Ni-Cr-Mo-W alloy is characterized by the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. To protect the surface of the substrate 13CrMo4-5 steel against aggressive environments the Inconel 686 as clad layer was used. The corrosion process was performed in oxidizing mixture of gases like O2, COx, SOx. The second part of corrosion Experiment concerned the corrosion test of the coating in reducing atmosphere of the specified gases with ashes, which contained e.g. Na, Cl, Ca, Si, C, Fe, Al.
Autor*innen: | Damian Koclęga, A. Radziszewska, Axel KranzmannORCiD, S. Dymek |
---|---|
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Aggressive environement; High temperature corrosion; Inconel 686; Laser Cladding; Material oxidation |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Veranstaltung: | Junior EUROMAT 2018 |
Veranstaltungsort: | Budapest, Hungary |
Beginndatum der Veranstaltung: | 08.07.2018 |
Enddatum der Veranstaltung: | 12.07.2018 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 02.08.2018 |
Referierte Publikation: | Nein |