Chloride ingress in cracked concrete: a laser induced breakdown spectroscopy (LIBS) study

  • Cracks are always present in reinforced concrete structures. In the presented research, influence of mechanical cracks on chloride ingress is studied. A compact reinforced concrete specimen was designed, mimicking the cracking behaviour of beam elements. Cracks of different widths were induced by means of mechanical loading. These cracked specimens were then subjected to weekly cycles of wetting and drying with NaCl solution. After the exposure, the specimens were cut, and chloride distributions were determined using Laser Induced Breakdown Spectroscopy (LIBS), an innovative technique which enables simultaneous determination of different elements with high spatial resolution and minimal specimen preparation. By combining element distributions of different elements, it is possible to discriminate between coarse aggregate particles, and the mortar matrix. It was found that the wider the crack is, the higher the ingress of chloride ions. This was, however, different for two testedCracks are always present in reinforced concrete structures. In the presented research, influence of mechanical cracks on chloride ingress is studied. A compact reinforced concrete specimen was designed, mimicking the cracking behaviour of beam elements. Cracks of different widths were induced by means of mechanical loading. These cracked specimens were then subjected to weekly cycles of wetting and drying with NaCl solution. After the exposure, the specimens were cut, and chloride distributions were determined using Laser Induced Breakdown Spectroscopy (LIBS), an innovative technique which enables simultaneous determination of different elements with high spatial resolution and minimal specimen preparation. By combining element distributions of different elements, it is possible to discriminate between coarse aggregate particles, and the mortar matrix. It was found that the wider the crack is, the higher the ingress of chloride ions. This was, however, different for two tested concrete mixes. Due to highly inhomogeneous chloride distribution around the cracks, use of fine-scale experimental techniques for chloride mapping is advised, based on the presented study.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 12_425.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:B. Savija, E. Schlangen, J. Pacheco, Steven Millar, Thorsten Eichler, Gerd Wilsch
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of advanced concrete technology
Jahr der Erstveröffentlichung:2014
Herausgeber (Institution):Japan Concrete Institute
Verlagsort:Tokyo
Jahrgang/Band:12
Ausgabe/Heft:10
Erste Seite:425
Letzte Seite:442
Freie Schlagwörter:Chloride; Concrete; Cracks; Ingress; LIBS
DOI:10.3151/jact.12.425
ISSN:1346-8014
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.11.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.