Purification of single walled carbon nanotubes by thermal gas phase oxidation

  • Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. ForSingle walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Sven Gajewski, Heinz-Eberhard Maneck, Uta Knoll, Dietmar Neubert, Ilona Dörfel, Reinhard Mach, Birgid Strauß, Jörg Florian Friedrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Diamond and related materials
Jahr der Erstveröffentlichung:2003
Verlag:Elsevier
Verlagsort:New York, NY
Jahrgang/Band:12
Ausgabe/Heft:3-7
Erste Seite:816
Letzte Seite:820
Freie Schlagwörter:Amorphous carbon; Cathodic arc discharge; Nanotubes; Oxidation
DOI:10.1016/S0925-9635(02)00362-X
ISSN:0925-9635
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:22.05.2003
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.