Recovery of chromium from AOD-converter slags

  • Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the highSlags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Burkart Adamczyk, Rudolf Brenneis, Christian AdamORCiD, D. Mudersbach
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Steel research international
Jahr der Erstveröffentlichung:2010
Verlag:Verl. Stahleisen
Verlagsort:Düsseldorf
Jahrgang/Band:81
Ausgabe/Heft:12
Erste Seite:1078
Letzte Seite:1083
Freie Schlagwörter:Arc furnace; By-product; Chromium recovery; High-alloyed steel; Reductive melting; Slag; Slag treatment; Thermochemical treatment
DOI:10.1002/srin.201000193
ISSN:1611-3683
ISSN:0177-4832
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:07.01.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.