Influence of differently structured aluminium-polypropylene interfaces on adhesion

  • Polar groups were introduced on polypropylene surfaces for increasing the surface energy and the peel strength to evaporated aluminium layers. Three kinds of plasma processes were used for introducing such functional groups to polyolefin surfaces: low-pressure radio-frequency (RF) O2 plasma exposure, atmospheric-pressure dielectric-barrier discharge (DBD) treatment in air, and the deposition of allylamine plasma polymer. The amino groups of the allylamine plasma polymer were also used as anchoring points for chemical introduction of covalently bonded spacer molecules equipped with reactive endgroups. Thus, silanol endgroups of a covalently bonded spacer were able to interact with the evaporated metal layer. The Al-PP composites achieved a maximal peel strength of 470 N/m by exposing the polymer to the lowpressure O2 plasma and 500 N/m on exposure to the atmospheric DBD plasma. After allylamine plasma polymerization and grafting of spacers, the peel strength was usually higher than 1500Polar groups were introduced on polypropylene surfaces for increasing the surface energy and the peel strength to evaporated aluminium layers. Three kinds of plasma processes were used for introducing such functional groups to polyolefin surfaces: low-pressure radio-frequency (RF) O2 plasma exposure, atmospheric-pressure dielectric-barrier discharge (DBD) treatment in air, and the deposition of allylamine plasma polymer. The amino groups of the allylamine plasma polymer were also used as anchoring points for chemical introduction of covalently bonded spacer molecules equipped with reactive endgroups. Thus, silanol endgroups of a covalently bonded spacer were able to interact with the evaporated metal layer. The Al-PP composites achieved a maximal peel strength of 470 N/m by exposing the polymer to the lowpressure O2 plasma and 500 N/m on exposure to the atmospheric DBD plasma. After allylamine plasma polymerization and grafting of spacers, the peel strength was usually higher than 1500 N/m and the composites could not be peeled.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Influence of differently structured aluminium-polypropylene interfaces on adhesion.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Huajie YinORCiD, Renate Mix, Jörg Florian Friedrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of adhesion science and technology
Jahr der Erstveröffentlichung:2011
Verlag:VNU Science Press
Verlagsort:Utrecht
Jahrgang/Band:25
Ausgabe/Heft:8
Erste Seite:799
Letzte Seite:818
Freie Schlagwörter:Dielectric barrier discharge (DBD); Low-pressure RF oxygen plasma; Peel strength; Polypropylene; Pulsed plasma polymerization; Surface wettability
DOI:10.1163/016942410X511132
ISSN:0169-4243
ISSN:1568-5616
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:07.07.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.