Structure of plasma-deposited poly(acrylic acid) films

  • Poly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that thePoly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating, where the reaction kinetics depends on DC.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Fahmy_et_al-2011-Plasma_Processes_and_Polymers.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:A. Fahmy, Renate Mix, Andreas SchönhalsORCiD, Jörg Florian Friedrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Plasma processes and polymers
Jahr der Erstveröffentlichung:2011
Verlag:Wiley-VCH Verl.
Verlagsort:Weinheim
Jahrgang/Band:8
Ausgabe/Heft:2
Erste Seite:147
Letzte Seite:159
DOI:10.1002/ppap.201000108
ISSN:1612-8850
ISSN:1612-8869
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:07.04.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.