Investigation of chloride-induced pitting corrosion of steel in concrete by a combination of electrochemical methods with X-ray tomography
- Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface.
Autor*innen: | Gino EbellORCiD, Jürgen Mietz, Andreas Burkert |
---|---|
Dokumenttyp: | Beitrag zu einem Tagungsband |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | EUROCORR 2014 - European corrosion congress |
Jahr der Erstveröffentlichung: | 2014 |
Herausgeber (Institution): | DECHEMA e.V. |
Erste Seite: | O-7207, 274-275 |
Freie Schlagwörter: | Chloride; Corrosion; Pitting corrosion; Rebar |
Veranstaltung: | EUROCORR 2014 - European corrosion congress |
Veranstaltungsort: | Pisa, Italy |
Beginndatum der Veranstaltung: | 08.09.2014 |
Enddatum der Veranstaltung: | 12.09.2014 |
ISBN: | 978-3-89746-159-8 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 25.09.2014 |