Investigation of chloride-induced pitting corrosion of steel in concrete by a combination of electrochemical methods with X-ray tomography

  • Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface.

Volltext Dateien herunterladen

  • O-7207.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Gino Ebell, Jürgen Mietz, Andreas Burkert
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):EUROCORR 2014 - European corrosion congress
Jahr der Erstveröffentlichung:2014
Organisationseinheit der BAM:7 Bauwerkssicherheit
7 Bauwerkssicherheit / 7.6 Korrosion und Korrosionsschutz
Herausgeber (Institution):DECHEMA e.V.
Erste Seite:O-7207, 274-275
Freie Schlagwörter:Chloride; Corrosion; Pitting corrosion; Rebar
Veranstaltung:EUROCORR 2014 - European corrosion congress
Veranstaltungsort:Pisa, Italy
Beginndatum der Veranstaltung:08.09.2014
Enddatum der Veranstaltung:12.09.2014
ISBN:978-3-89746-159-8
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:25.09.2014