Geopolymerization of a silica residue from waste treatment of chlorosilane production

  • A silica residue from waste treatment of chlorosilane production was used together with solid sodium aluminate to test its applicability for the production of one-part geopolymers. The blend was activated with water and cured at 70 °C. The degree of reaction and strength were determined after 1, 3, and 7 days. The reaction products were analyzed by XRD and SEM/EDX. Until the third day of curing the degree of reaction of the residue reached 51 % and the strength was 8.9 MPa. The reaction product was identified as geopolymer containing zeolite A. Thus, the results confirmed that the residue may be used in the production of geopolymers. However, after 3 days of curing no further progress of reaction was observed and the strength slightly decreased, which was attributed to changes in the structure of the geopolymeric gel. It was further observed that even harsh vacuum drying left some water (presumably zeolitic water and surface hydroxyl groups) in the geopolymer.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Gregor GluthORCiD, Christian Lehmann, Katrin RübnerORCiD, Hans-Carsten KühneORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials and structures
Jahr der Erstveröffentlichung:2013
Verlag:Springer
Verlagsort:Dordrecht
Jahrgang/Band:46
Ausgabe/Heft:8
Erste Seite:1291
Letzte Seite:1298
Freie Schlagwörter:Geopolymers; One-part formulation; Silica; Zeolite A
DOI:10.1617/s11527-012-9972-5
URL:http://link.springer.com/article/10.1617/s11527-012-9972-5/fulltext.html
ISSN:1359-5997
ISSN:1871-6873
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:03.06.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.