Synthesis, characterization and properties of hierarchically assembled antimony oxyhalides nanonetworks

  • The novel synthesis route has been developed for hierarchically structured; nanorods and nanosheets of Sb4O5Cl2 from a single precursor, with dimension range between 57–90 nm. X-ray powder diffraction analysis confirmed the monoclinic crystal symmetry in P21/c(14)with structure type Sb4O5Cl2 for both forms; the nanorods and nanosheets. Rietveld refinements and crystallite size investigations of the powder patterns revealed significant enhancement in intensity with subtle variation in the lattice parameters and crystallite size decrease in case of nanosheets in comparison to the nanorods assembly. Through scanning electron microscopy, a composition commensurate to Sb4O5Cl2 at% with averaged dimensions; dia.∼90 nm, l ∼ 2 μm for nanorods and dia.∼50–150 nm for nanosheets got corroborated. Owing to the quantum confinement a band gap widening was observed while moving from bulk to nano regime, i.e. 3.25, 3.31 and 3.34 eV, for bulk, nanosheets, and nanorods, respectively. In the case ofThe novel synthesis route has been developed for hierarchically structured; nanorods and nanosheets of Sb4O5Cl2 from a single precursor, with dimension range between 57–90 nm. X-ray powder diffraction analysis confirmed the monoclinic crystal symmetry in P21/c(14)with structure type Sb4O5Cl2 for both forms; the nanorods and nanosheets. Rietveld refinements and crystallite size investigations of the powder patterns revealed significant enhancement in intensity with subtle variation in the lattice parameters and crystallite size decrease in case of nanosheets in comparison to the nanorods assembly. Through scanning electron microscopy, a composition commensurate to Sb4O5Cl2 at% with averaged dimensions; dia.∼90 nm, l ∼ 2 μm for nanorods and dia.∼50–150 nm for nanosheets got corroborated. Owing to the quantum confinement a band gap widening was observed while moving from bulk to nano regime, i.e. 3.25, 3.31 and 3.34 eV, for bulk, nanosheets, and nanorods, respectively. In the case of nanosheets, the highest value of dielectric constant was observed, i.e. 87, as compared to nanorods and the bulk, i.e. 40 and 35.5, respectively. The nanosheets also showed the highest value of dielectric and tangent loss with an increase in frequency due to the least crystallite size of these nanonetworks. Nanosheets depicted the higher AC conductivity at low frequency due to the alignment of the charges but its value decreases at the higher frequency due to lack of time for charge reorientation. The hopping phenomenon was observed in all three cases with the most prominent one in bulk case at higher frequencies.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Paper Ali.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Naveed Ali, N. Komal, Z. Malik, A.J. Chaudhary
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials research express
Jahr der Erstveröffentlichung:2019
Organisationseinheit der BAM:6 Materialchemie
6 Materialchemie / 6.3 Strukturanalytik
Verlag:IOP
Jahrgang/Band:6
Ausgabe/Heft:6
Erste Seite:065035
DDC-Klassifikation:Naturwissenschaften und Mathematik / Chemie / Analytische Chemie
Freie Schlagwörter:Antimony oxychloride ( Sb4O5Cl2); Dielectric properties; Nanorods; Nanosheets; Optical properties
Themenfelder/Aktivitätsfelder der BAM:Chemie und Prozesstechnik
DOI:10.1088/2053-1591/ab0da9
ISSN:2053-1591
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:08.04.2019
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:08.04.2019
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.