Lattice distortion in precipitates of single crystal superalloy SC16 under creep deformation

  • Specimens of single crystal superalloy SC16 were creep deformed at 1223 K along [0 0 1] up to ±0.5% creep strain using stresses of -150 MPa and +150 MPa, respectively. Line widths and peak positions of superlattice reflections were measured by means of X-ray diffraction parallel and perpendicular to the load axis in the temperature range between 293 K and 1173 K. The line widths were found to decrease with the increase of temperature for both directions on the two specimens after tensile and compressive creep deformation. After both kinds of creep deformation the crystal lattice showed tetragonal distortion which decreased with increasing temperature. The tetragonality after tensile creep deformation was larger than unity while it was smaller than unity after compressive creep deformation. The peak positions and widths restored after cooling back to room temperature. The experimental results can qualitatively be explained by the creation of dislocations during deformation and theirSpecimens of single crystal superalloy SC16 were creep deformed at 1223 K along [0 0 1] up to ±0.5% creep strain using stresses of -150 MPa and +150 MPa, respectively. Line widths and peak positions of superlattice reflections were measured by means of X-ray diffraction parallel and perpendicular to the load axis in the temperature range between 293 K and 1173 K. The line widths were found to decrease with the increase of temperature for both directions on the two specimens after tensile and compressive creep deformation. After both kinds of creep deformation the crystal lattice showed tetragonal distortion which decreased with increasing temperature. The tetragonality after tensile creep deformation was larger than unity while it was smaller than unity after compressive creep deformation. The peak positions and widths restored after cooling back to room temperature. The experimental results can qualitatively be explained by the creation of dislocations during deformation and their anisotropic arrangement at the γ/γ' interfaces.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:W. Chen, N. Darowski, I. Zizak, G. Schumacher, Hellmuth Klingelhöffer, W. Neumann
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Nuclear instruments and methods in physics research B
Jahr der Erstveröffentlichung:2006
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:246
Ausgabe/Heft:1
Erste Seite:201
Letzte Seite:205
Freie Schlagwörter:Creep deformation; Lattice distortion; Superalloys
DOI:10.1016/j.nimb.2005.12.032
ISSN:0168-583X
ISSN:1872-9584
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:29.06.2006
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.