In-situ observation of sub-critical crack growth in water bearing borate glasses

  • 185 cracks were initiated in a soda-lime-silica glass by Vickers indentation and grown under controlled dry nitrogen atmosphere. Direct observation of subcritical crack growth (SCCG) upon indentation was performed using a video camera with an image acquisition rate of 3 ms. The results show that the validity of K(c) relations used to determine the indentation fracture toughness from a single imprint is questionable. It seems that correlation of crack length to stress intensity necessitate the use of statistical significant data of multiple crack events.

Volltext Dateien herunterladen

  • Publica_PK_FFAG_Aalborg_2017.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:P. Kiefer
Koautoren/innen:R. Balzer, H. Behrens, Stefan Reinsch, Ralf Müller, J. Deubener
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.6 Glas
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Glass; Indentation fracture toughness; Sub critical crack growth; Vickers; Water bearing glass
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Degradation von Werkstoffen und Materialien
Veranstaltung:FFAG 7: 7th International Workshop on Flow and Fracture of Advanced Glasses
Veranstaltungsort:Aalborg, Denmark
Beginndatum der Veranstaltung:02.07.2017
Enddatum der Veranstaltung:05.07.2017
Verfügbarkeit des Volltexts:Volltext-PDF im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:22.02.2018
Referierte Publikation:Nein