In-situ observation of sub-critical crack growth in water bearing borate glasses
- 185 cracks were initiated in a soda-lime-silica glass by Vickers indentation and grown under controlled dry nitrogen atmosphere. Direct observation of subcritical crack growth (SCCG) upon indentation was performed using a video camera with an image acquisition rate of 3 ms. The results show that the validity of K(c) relations used to determine the indentation fracture toughness from a single imprint is questionable. It seems that correlation of crack length to stress intensity necessitate the use of statistical significant data of multiple crack events.
Autor*innen: | P. Kiefer |
---|---|
Koautor*innen: | R. Balzer, H. Behrens, Stefan ReinschORCiD, Ralf Müller, J. Deubener |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2017 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Glass; Indentation fracture toughness; Sub critical crack growth; Vickers; Water bearing glass |
Veranstaltung: | FFAG 7: 7th International Workshop on Flow and Fracture of Advanced Glasses |
Veranstaltungsort: | Aalborg, Denmark |
Beginndatum der Veranstaltung: | 02.07.2017 |
Enddatum der Veranstaltung: | 05.07.2017 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 22.02.2018 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |