Thermo-Mechanical Fatigue Behavior of P92

  • In the present contribution, the thermo-mechanical fatigue and creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard LCF/TMF-tests as well as near-service loading tests with different hold times have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics (like e.g. pronounced softening) and the dominating damage mechanisms under different loads. The test programme is complemented by selected tests on service-aged material which demonstrate possible reactions of older components in existing plants to changes in operation profiles. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior.

Volltext Dateien herunterladen

  • LCF08_Vortrag.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Maria Jürgens
Koautoren/innen:Birgit Skrotzki
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik
Freie Schlagwörter:Ferritic-martensitic steels; Near-service testing; P91; P92; Power plant; Thermo-Mechanical Fatigue
Themenfelder/Aktivitätsfelder der BAM:Energie
Veranstaltung:LCF08
Veranstaltungsort:Dresden, Germany
Beginndatum der Veranstaltung:27.06.2017
Enddatum der Veranstaltung:29.06.2017
Verfügbarkeit des Volltexts:Volltext-PDF im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:04.10.2017
Referierte Publikation:Nein