Reinforced concrete slabs strengthened with textile reinforced concrete subjected to fire

  • Thin layers of textile reinforced concrete (TRC) can be used as strengthening for reinforced concrete (RC) slabs or beams to increase their foad-bearing capacity. The concrete matrix consists of a fine-grained concrete with a thickness of 8 to 15 mm. Information on the behaviour of strengthened structures subjected to fire is of particular inlerest for practical applications of this innovative construction method. A total of 7 RC slabs with Steel reinforcement were produced: 2 slabs were used as reference and 5 slabs were strengthened with three layers of textile reinforcement. Ultimate capacity of reference slabs and particular TRC strengthened slabs was determined from statie load results fom 4-point-bending tests. Fire tests on these slabs were carried out with utilization fectors using a Standard temperature curve (ISO-834-1) for fire testing. Test loads varied between 0 % and 65 % ofuMmate load. To detect temperatures during fire exposure thermocouples were arranged throughoutThin layers of textile reinforced concrete (TRC) can be used as strengthening for reinforced concrete (RC) slabs or beams to increase their foad-bearing capacity. The concrete matrix consists of a fine-grained concrete with a thickness of 8 to 15 mm. Information on the behaviour of strengthened structures subjected to fire is of particular inlerest for practical applications of this innovative construction method. A total of 7 RC slabs with Steel reinforcement were produced: 2 slabs were used as reference and 5 slabs were strengthened with three layers of textile reinforcement. Ultimate capacity of reference slabs and particular TRC strengthened slabs was determined from statie load results fom 4-point-bending tests. Fire tests on these slabs were carried out with utilization fectors using a Standard temperature curve (ISO-834-1) for fire testing. Test loads varied between 0 % and 65 % ofuMmate load. To detect temperatures during fire exposure thermocouples were arranged throughout the cross-section of the slabs. Depending on the utilization the slabs were exposed to fire for 30 minutes or for 60 minutes. In some cases bending fäilure occurred, in other cases the slabs survived. None of the specimens exhibited any visual damage or concrete spalling during fire exposure. Results of deformation measurements and residual strength measurements are presented. Even though mechanisms are not fifily understood, it is important to discuss the presumable reasons for the surprisingiy positive test results. It is presumed tbat the key mechanisms contributing to the outstanding fire resistance capability presented are: superior crack control of the TRC and load redistribution between textile and Steel reinforcement as well as the primary load transfer directly into the slabs.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • REINFORCED CONCRETE SLABS STRENGTHENED WITH TEXTILE.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:D. Ehlig, Sascha HothanORCiD
Persönliche Herausgeber*innen:E.A.B. Koenders, F. Dehn
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):2nd International RILEM workshop on concrete spalling due to fire exposure (Proceedings)
Jahr der Erstveröffentlichung:2011
Verlag:RILEM Publications
Jahrgang/Band:PRO 80
Erste Seite:419
Letzte Seite:426
Freie Schlagwörter:Bending load; Carbon fibres; Fine-grained concrete; Fire exposure; Textile reinforced concrete
Veranstaltung:2nd International RILEM workshop on concrete spalling due to fire exposure
Veranstaltungsort:Delft, The Netherlands
Beginndatum der Veranstaltung:05.10.2011
Enddatum der Veranstaltung:07.10.2011
ISBN:978-2-35158-118-6
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.