In situ study of structural integrity of low transformation temperature (LTT)-welds

  • We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as aWe discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S0921509311003753-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:J. Altenkirch, J. Gibmeier, Arne KrommORCiD, Thomas KannengießerORCiD, T. Nitschke-Pagel, M. Hofmann
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials science and engineering A
Jahr der Erstveröffentlichung:2011
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:528
Ausgabe/Heft:16-17
Erste Seite:5566
Letzte Seite:5575
Freie Schlagwörter:Low transformation temperature; Neutron diffraction; Residual stress
DOI:10.1016/j.msea.2011.03.091
ISSN:0921-5093
ISSN:1873-4936
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:26.09.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.