Compatibility of polyehtylene grades with biofuels and biodiesel-heating oil blends

  • The aim of this work was to study the interaction between high density polyethylene (HDPE) grades as material for dangeraus goods packagings and biofuels such as E10 (fuel with 10% ethanol), E85 (fuel with 85% ethanol), biodiesei and 810 (heating oil with 10% biodiesel). Jerricans made of two polyethylene grades were filled with these fuels and exposed to temperatures of 20 oc and 40 oc for more than one year. Tensile properlies (tensile strength, breaking elongation and elasticity modulus) and Melt Flow Rate (MFR) were determined, and Fourier Transform Infrared Spectroscopy (FTIR) was used to evaluate changes in the chemical structure. Measurements of the MFR and tensile properlies of the polyethylene grades after exposure to E1 0, E85 and 810 showed only a slightly damaging influence. A n increase in the peak of 1585 cm·1 for the (C=C) stretching vibrations was visible in the FTIR spectra after immersion tests with E85. A n increase in the MFR with the immersion time of the gradesThe aim of this work was to study the interaction between high density polyethylene (HDPE) grades as material for dangeraus goods packagings and biofuels such as E10 (fuel with 10% ethanol), E85 (fuel with 85% ethanol), biodiesei and 810 (heating oil with 10% biodiesel). Jerricans made of two polyethylene grades were filled with these fuels and exposed to temperatures of 20 oc and 40 oc for more than one year. Tensile properlies (tensile strength, breaking elongation and elasticity modulus) and Melt Flow Rate (MFR) were determined, and Fourier Transform Infrared Spectroscopy (FTIR) was used to evaluate changes in the chemical structure. Measurements of the MFR and tensile properlies of the polyethylene grades after exposure to E1 0, E85 and 810 showed only a slightly damaging influence. A n increase in the peak of 1585 cm·1 for the (C=C) stretching vibrations was visible in the FTIR spectra after immersion tests with E85. A n increase in the MFR with the immersion time of the grades in biodiesei was measured - in parlicular, after one year of exposure. The elasticity modulus of the polyethylene grades was reduced with the immersion time too. The FTIR spectra showed a broadening of the C=O peak of 1740 cm·1 and the appearance of the hydroxyl group at 3500 cm·1.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Weltschev_Compatibility of polyehtylene grades.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Margit Weltschev, Anka Kohl, Manuela Haufe, Martina Heyer
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Corrosion 2015
Jahr der Erstveröffentlichung:2015
Herausgeber (Institution):NACE International
Erste Seite:Paper No. 5536, 1
Letzte Seite:12
Freie Schlagwörter:B10; Biodiesel; Biofuels; Change in MFR and tensile properties; Compatibility; E10; E85; FTIR analysis; Polyethylene grades; Tensile properties
Veranstaltung:Corrosion 2015
Veranstaltungsort:Dallas, TX, USA
Beginndatum der Veranstaltung:15.03.2015
Enddatum der Veranstaltung:19.03.2015
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.04.2015
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.