Compatibility of high-density polyethylene grades with biofuels

  • The aim of this work was to study the interaction between high-density polyethylene (HDPE) grades as material for dangerous goods packagings and biofuels such as E85 and biodiesel. Jerricans made of two polyethylene (PE) grades were filled with these fuels and exposed to temperatures of 20°C and 40°C for 1 year. Tensile properties (tensile strength, breaking elongation and elasticity modulus) and melt flow rate (MFR) were determined once a month, and Fourier transform infrared (FTIR) spectroscopy was used to evaluate changes in the chemical structure. Measurements of the MFR and tensile properties of the PE grades after 1 year of exposure to E85 showed only a slightly damaging influence. An increase in the peak of 1585 cm-1 (C=C) stretching vibrations is visible in the FTIR spectra after the immersion tests with E85. Therefore, packagings made of HDPE grades are suitable for the transport of E85. An increase in the MFR with immersion time of the grades in biodiesel was measured,The aim of this work was to study the interaction between high-density polyethylene (HDPE) grades as material for dangerous goods packagings and biofuels such as E85 and biodiesel. Jerricans made of two polyethylene (PE) grades were filled with these fuels and exposed to temperatures of 20°C and 40°C for 1 year. Tensile properties (tensile strength, breaking elongation and elasticity modulus) and melt flow rate (MFR) were determined once a month, and Fourier transform infrared (FTIR) spectroscopy was used to evaluate changes in the chemical structure. Measurements of the MFR and tensile properties of the PE grades after 1 year of exposure to E85 showed only a slightly damaging influence. An increase in the peak of 1585 cm-1 (C=C) stretching vibrations is visible in the FTIR spectra after the immersion tests with E85. Therefore, packagings made of HDPE grades are suitable for the transport of E85. An increase in the MFR with immersion time of the grades in biodiesel was measured, in particular, after 1 year of exposure. The elasticity modulus of the PE grades was reduced with immersion time. The FTIR spectra showed a broadening of the CO peak of 1740 cm-1 and the appearance of the hydroxyl group at 3500 cm-1. Both results are explained by secondary degradation products of the PE decomposition process caused by increasing unsaturated fatty acid content in the biodiesel. In light of the above mentioned, it was concluded that HDPE grades are not suitable as packaging materials for the transport of biodiesel.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Weltschev_et_al-2014-Packaging_Technology_and_Science.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Margit Weltschev, Jan Werner, Manuela Haufe, Martina Heyer
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Packaging technology & science
Jahr der Erstveröffentlichung:2013
Verlag:Wiley
Verlagsort:Chichester, UK
Jahrgang/Band:27
Erste Seite:231
Letzte Seite:240
Freie Schlagwörter:Biodiesel; E85; FTIR analysis; Polyethylene grades; Tensile properties
Veranstaltung:IAPRI 2013 - 26th Symposium on packaging
Veranstaltungsort:Espoo, Finland
Beginndatum der Veranstaltung:10.06.2013
Enddatum der Veranstaltung:13.06.2013
DOI:10.1002/pts.2028
ISSN:0894-3214
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:20.06.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.