Surface modification of carbon nanofibers by glycidoxysilane for altering the conductive and mechanical properties of epoxy composites

  • Carbon nanofibers (CNFs) were functionalized with 3-glycidoxypropyltrimethoxysilane and dispersed into epoxy resin. The chemical modification of CNFs was confirmed by FTIR, SEM, EDX and TGA measurements. After silanization, FTIR showed the existance of epoxy ring; EDX detected Si element; while TGA indicated 1.1 wt.% Si on CNFs. Mechanical properties were analyzed by DMA. Silanized CNFs/epoxy composites demonstrated improved dispersion of CNFs in the matrix, and an enhancement of storage modulus for about 20% compared to the neat matrix, which indicated that the modification of CNFs improved the adhesion between fillers and matrices. DC electrical conductivity of CNFs was reduced about 7-fold compared to the original CNFs due to the silane coating. Accordingly, the composites containing silanized CNFs also had lower electrical conductivity than those containing original CNFs. In spite of decreased electrical conductivity, thermal conductivity of silanized CNFs/epoxy composites wasCarbon nanofibers (CNFs) were functionalized with 3-glycidoxypropyltrimethoxysilane and dispersed into epoxy resin. The chemical modification of CNFs was confirmed by FTIR, SEM, EDX and TGA measurements. After silanization, FTIR showed the existance of epoxy ring; EDX detected Si element; while TGA indicated 1.1 wt.% Si on CNFs. Mechanical properties were analyzed by DMA. Silanized CNFs/epoxy composites demonstrated improved dispersion of CNFs in the matrix, and an enhancement of storage modulus for about 20% compared to the neat matrix, which indicated that the modification of CNFs improved the adhesion between fillers and matrices. DC electrical conductivity of CNFs was reduced about 7-fold compared to the original CNFs due to the silane coating. Accordingly, the composites containing silanized CNFs also had lower electrical conductivity than those containing original CNFs. In spite of decreased electrical conductivity, thermal conductivity of silanized CNFs/epoxy composites was increased due to the surface modification of CNFs.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Yaru Nie, Thomas Hübert
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Composites / A
Jahr der Erstveröffentlichung:2012
Verlag:Elsevier
Verlagsort:Oxford
Jahrgang/Band:43
Ausgabe/Heft:8
Erste Seite:1357
Letzte Seite:1364
Freie Schlagwörter:A. Polymer-matrix composites (PMCs); B. Electrical properties; B. Mechanical properties; B. Thermal properties
DOI:10.1016/j.compositesa.2012.03.025
ISSN:1359-835X
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:25.06.2012
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.