Electrical Properties of Carbon Black and Ruthenium Dioxide Embedded Silica Films

  • The electrical properties of sol–gel-derived films can be tailored by embedding conductive particles of ruthenium dioxide or carbon black in an insulating amorphous SiO2 silica matrix. The preparation process included an acid hydrolysis of tetraethoxysilane and methyltrimethoxysilane. Then alcohol solutions of ruthenium chloride or carbon black were added. Films of filler concentration up to 60 vol.% were prepared by dip coating and then dried and heat-treated at various temperatures up to 600_°C. The D.C. resistance of the films can be varied within the range of 109 to 10–2 OHgr sdot cm. A non-linear dependence on filler composition in the films was observed for both systems, which is explained by a modified percolation theory. A percolation threshold of 5.5 vol.% for SiO2-RuO2 or 50 vol.% for SiO2-C films, whereby the resistance drastically decreases, was determined. Moreover the temperature dependency of resistance and the current-voltage characteristics of the films can also beThe electrical properties of sol–gel-derived films can be tailored by embedding conductive particles of ruthenium dioxide or carbon black in an insulating amorphous SiO2 silica matrix. The preparation process included an acid hydrolysis of tetraethoxysilane and methyltrimethoxysilane. Then alcohol solutions of ruthenium chloride or carbon black were added. Films of filler concentration up to 60 vol.% were prepared by dip coating and then dried and heat-treated at various temperatures up to 600_°C. The D.C. resistance of the films can be varied within the range of 109 to 10–2 OHgr sdot cm. A non-linear dependence on filler composition in the films was observed for both systems, which is explained by a modified percolation theory. A percolation threshold of 5.5 vol.% for SiO2-RuO2 or 50 vol.% for SiO2-C films, whereby the resistance drastically decreases, was determined. Moreover the temperature dependency of resistance and the current-voltage characteristics of the films can also be explained by this geometric model.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Thomas Hübert, Aki Shimamura, Andreas Klyszcz
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of sol gel science and technology
Jahr der Erstveröffentlichung:2004
Verlag:Kluwer Academic Publ.
Verlagsort:Dordrecht
Jahrgang/Band:32
Erste Seite:131
Letzte Seite:135
Freie Schlagwörter:Carbon black; Percolation phenomena; Ruthenium dioxide; Sol-gel; Thin films
DOI:10.1007/s10971-004-5777-5
ISSN:0928-0707
ISSN:1573-4846
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:14.02.2005
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.