Time-resolved Bragg-edge neutron radiography for observing martensitic phase transformation from austenitized super martensitic steel

  • Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial resolution of 100 µm.

Volltext Dateien herunterladen

  • 2017-Dabah-J Mater Sc.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Eitan Dabah, Beate Pfretzschner, Thomas Schaupp, N. Kardjilov, I. Manke, M. Boin, R. Woracek, Axel Griesche
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of Materials Science
Jahr der Erstveröffentlichung:2017
Organisationseinheit der BAM:9 Komponentensicherheit
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen
Jahrgang/Band:52
Ausgabe/Heft:6
Erste Seite:3490
Letzte Seite:3496
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Bragg-edge imaging; Neutron imaging; Phase transformation
Themenfelder/Aktivitätsfelder der BAM:Material
DOI:https://doi.org/10.1007/s10853-016-0642-9
URL:http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=Alerting&SrcApp=Alerting&DestApp=WOS&DestLinkType=FullRecord;UT=WOS:000390125500045
ISSN:0022-2461
ISSN:1573-4803
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.12.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:13.01.2017