3D imaging of hydrogen assisted cracking in metals using refraction enhanced synchrotron CT

  • Hydrogen in metals can cause a degradation of the mechanical properties with possible subsequent hydrogen assisted cracking (HAC). Though, the mechanism of HAC is not completely understood yet and thus suitable methods for in situ investigations to characterise the crack formation are needed. X-ray computed tomography (CT) is a well-known tool for analysing these properties. However, the effective resolution of the detector system limits the detection of small defects by CT. Analyser based imaging (ABI) takes advantage of x-ray refraction at interfaces between volumes of different density, i.e. of cracks, pores, inclusions, etc., within the sample to detect defects smaller than the resolution of the detector system. In this study, measurements on an aluminium alloy weld showed that ABI allows us to resolve the 3D structure of cracks undetected by absorption based CT. Prospective investigations will analyse HAC in steels.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:René Laquai, Thomas Schaupp, Bernd R. Müller, Axel Griesche, Giovanni Bruno, Thomas Kannengießer
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):NDT-CE 2015 - International symposium non-destructive testing in civil engineering (Proceedings)
Jahr der Erstveröffentlichung:2015
Organisationseinheit der BAM:8 Zerstörungsfreie Prüfung
8 Zerstörungsfreie Prüfung / 8.5 Mikro-ZfP
9 Komponentensicherheit
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen
Herausgeber (Institution):Technische Universität Berlin / Bundesanstalt für Materialforschung und -prüfung
Erste Seite:1217
Letzte Seite:1224
Freie Schlagwörter:Aluminium alloy; Analyser based imaging; CT; Computed tomography (CT); Hydrogen assisted cracking (HAC); Hydrogen embrittlement (HE); Röntgenrefraktion; Synchrotron radiation; Wasserstoffunterstützte Rissbildung; Wasserstoffversprödung; X-ray refraction
Veranstaltung:NDT-CE 2015 - International symposium non-destructive testing in civil engineering
Veranstaltungsort:Berlin, Germany
Beginndatum der Veranstaltung:2015-09-15
Enddatum der Veranstaltung:2015-09-17
ISSN:1435-4934
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein