In Vivo Effects of Coating Loaded and Unloaded Ti Implants with Collagen, Chondroitin Sulfate, and Hydroxyapatite in the Sheep Tibia

  • The in vivo effects of coating titanium implants with organic extracellular matrix molecules were examined in the sheep tibia. Titanium screws (5.0 mm) were coated with type I collagen (Ti/Coll) or type I collagen and chondroitin sulfate (Ti/Coll/CS) by biomimetic fibrillogenesis. Uncoated screws (Ti) and screws coated with hydroxyapatite (Ti/HA) served as control. Six adult female sheep received one screw of each type to stabilize a midshaft tibial fracture with external fixation. Four cylindrical implants of 4-mm outer diameter and 3.3-mm inner diameter with the same coatings were inserted into the tibial head. No pin track infections were seen at the time of implant retrieval 6 weeks after implantation. Extraction torque was greater for Ti/HA (1181 Nmm) and Ti/Coll/CS (1088 Nmm) compared to Ti/Coll (900 Nmm) and Ti (904 Nmm) [N.S.]. Newly formed bone was noted around all coated screws within the medullary cavity. Macrophage and osteoclast activity was significantly reduced aroundThe in vivo effects of coating titanium implants with organic extracellular matrix molecules were examined in the sheep tibia. Titanium screws (5.0 mm) were coated with type I collagen (Ti/Coll) or type I collagen and chondroitin sulfate (Ti/Coll/CS) by biomimetic fibrillogenesis. Uncoated screws (Ti) and screws coated with hydroxyapatite (Ti/HA) served as control. Six adult female sheep received one screw of each type to stabilize a midshaft tibial fracture with external fixation. Four cylindrical implants of 4-mm outer diameter and 3.3-mm inner diameter with the same coatings were inserted into the tibial head. No pin track infections were seen at the time of implant retrieval 6 weeks after implantation. Extraction torque was greater for Ti/HA (1181 Nmm) and Ti/Coll/CS (1088 Nmm) compared to Ti/Coll (900 Nmm) and Ti (904 Nmm) [N.S.]. Newly formed bone was noted around all coated screws within the medullary cavity. Macrophage and osteoclast activity was significantly reduced around Ti/Coll/CS in both types of implants compared to uncoated controls (p < 0.05). Osteoblast activity was significantly increased around loaded Ti/Coll and Ti/Coll/CS screws compared to uncoated Ti screws (p < 0.05). Microtomographic evaluation (SRµCT) revealed no significant differences in new bone formation around the unloaded tibial head implants.Coating of external fixation devices with of type I collagen and chondroitin sulfate appears to have similar effects with respect to stability and bone healing as HA but with less osteoclast activity. These findings were more pronounced under loaded than unloaded conditions in the sheeptibia.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:S. Rammelt, C. Heck, R. Bernhardt, S. Bierbaum, D. Scharnweber, Jürgen Goebbels, J. Ziegler, A. Biewener, H. Zwipp
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of Orthopaedic Research
Jahr der Erstveröffentlichung:2007
Verlag:Wiley
Verlagsort:Hoboken, NJ
Jahrgang/Band:25
Ausgabe/Heft:8
Erste Seite:1052
Letzte Seite:1061
Freie Schlagwörter:Bone implants; Chondroitin sulfate; Coating; Collagen; External fixation; titanium
DOI:10.1002/jor.20403
ISSN:0736-0266
ISSN:1554-527X
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:20.09.2007
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.