Fracture mechanics on microscale of composite plies under transverse loading
- The energy release rate delivered during the debonding of a fiber inside a composite ply is analysed using a representative volume element. Two different fiber volume fractions are studied by a linear elastic fracture mechanical analysis by using the finite element method. The dependency of the mixed mode energy release rate on the length of the crack increment is analysed. It is shown that the same general behaviour found in case of a straight Interface crack is valid also for circular cracks. As a result the discrimination of the energy release rate into mode I and mode II portions is questionable.
Autor*innen: | Christian Marotzke, Titus Feldmann |
---|---|
Dokumenttyp: | Beitrag zu einem Tagungsband |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | ECCM16 - 16th European conference on composite materials |
Jahr der Erstveröffentlichung: | 2014 |
Herausgeber (Institution): | Universidad de Sevilla |
Erste Seite: | 0472-1 |
Letzte Seite: | 0472-8 |
Freie Schlagwörter: | Composite; Energy release rate; Interface crack; Mode mixity |
Veranstaltung: | ECCM16 - 16th European conference on composite materials |
Veranstaltungsort: | Seville, Spain |
Beginndatum der Veranstaltung: | 22.06.2014 |
Enddatum der Veranstaltung: | 26.06.2014 |
ISBN: | 978-84-616-9798-4 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 11.08.2014 |