Damage evolution of Al matrix 4-phase composite

  • The evolution of the microstructure of multiphase metal matrix composite AlSi12CuNiMg with 7% vol. Al2O3 + 15% vol. SiC (short fibers and whiskers, respectively) was studied by synchrotron computed tomography. It comprehended as cast and after heat treatment conditions, as well as damage evaluation after ex-situ compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and damage events are studied. The influence on mechanical properties of the orientation of the planar random short fibres Al2O3 towards loading was investigated. Phase-specific load partition analysis for samples with fiber plane parallel and orthogonal to load, respectively, was performed by means of neutron diffraction (ND) during in-situ compression tests at room temperature. ND results proved that damage occurrence in the fillers strongly depends on the preferential orientation of those, playing a crucial role in the failure of the sample. The computedThe evolution of the microstructure of multiphase metal matrix composite AlSi12CuNiMg with 7% vol. Al2O3 + 15% vol. SiC (short fibers and whiskers, respectively) was studied by synchrotron computed tomography. It comprehended as cast and after heat treatment conditions, as well as damage evaluation after ex-situ compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and damage events are studied. The influence on mechanical properties of the orientation of the planar random short fibres Al2O3 towards loading was investigated. Phase-specific load partition analysis for samples with fiber plane parallel and orthogonal to load, respectively, was performed by means of neutron diffraction (ND) during in-situ compression tests at room temperature. ND results proved that damage occurrence in the fillers strongly depends on the preferential orientation of those, playing a crucial role in the failure of the sample. The computed tomography observations confirm the damage observations from curves of load partition analysis of each phase.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Cabeza_NDT_12072017_final.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:S. Cabeza, Giovanni BrunoORCiD
Koautor*innen:Tatiana Mishurova, G. Garces, G. Requena
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Aluminium matrix; Composites; Computed tomography; Neutron diffraction
Veranstaltung:FiMPART 2017
Veranstaltungsort:Bordeaux, France
Beginndatum der Veranstaltung:9.7.2017
Enddatum der Veranstaltung:12.7.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:25.07.2017
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.